The electrochemical properties of C/MnO₂ composite materials in 1 M sodium sulfate solution were investigated using the methods of cyclic voltammetry, galvanostatic charge-discharge and impedance spectroscopy. It was shown that the capacitive characteristics of the electrodes depend on the nature and the method of obtaining manganese oxide nanoparticles. It was established that the material containing manganese oxide obtained using isoamyl alcohol as a reducing agent has high electrochemical characteristics.

The electrochemical characteristics of the electrode material based on activated “NORIT B Test EUR” carbon in 1 M sodium sulfate solution were evaluated by cyclic voltammetry, galvanostatic charge-discharge curves, and impedance spectroscopy. It is established that this material has low resistance, and the specific capacity of the electrode was 45 F/g.

DOI: 10.18500/1608-4039-2015-15-4-160-166

Behavior of electrodes based on activated carbon P2 (Ener G2) wih additions of plain carbon black, as well as carbon black doped with silver nanoparticles have been studied. Depending on potential range and polarization direction the electrodes were found to reveal a capacitance close to double-layer or pseudocapacitance.

A various features of the electrochemical behavior of number superfine carbon materials in electrolyte based on an ionic liquid 1-methyl-3-butilimidazolium tetrafluorineborate (1Me3BuImBF4) were determined by voltammetry and impedance methods. A comparative analysis of the effect of the type and nature of the electrolyte material on the main electrochemical characteristics of carbon electrodes which may be used in supercapacitors was done.

There are the tests results of the symmetrical carbon super-capacitors (on the sulfuric acid electrolyte), whose electrodes are prepared with two methods (spraying and calendering) from two coals: coal of brand XH-00W1 (China) and coal, developed by the authors together with the Latvian state institute of wood chemistry. It is shown that the specific characteristics of super-capacitor substantially depend on the specific mass of electrodes (mg/sm²), and also from the method of their production.